LUVOCOM® 1301-8558 Datasheet,PPS,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1301-8558 is a polyphenylene sulfide (PPS) material, which contains a glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1301-8558 are: Flame Retardant High stiffness high strength Creep resistance chemical resistance Typical application areas include: engineering/industrial accessories textile/fiber Automotive Industry business/office supplies medical/health care

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	PTFE lubricant
Features	Low friction coefficient Rigidity, high High strength Good creep resistance Good chemical resistance Good wear resistance Heat resistance, high Lubrication Flame retardancy
Uses	Pump parts Gear Textile applications Engineering accessories Application in Automobile Field Business equipment Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.69	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.050	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ISO 527-2
Tensile Stress (Break)	115	MPa	ISO 527-2
Tensile Strain (Yield)	1.5	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	180	MPa	ISO 178
Flexural Strain at Flexural Strength	2.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	240	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	250	°C	ISO 75-2/A
Continuous Use Temperature	220	°C	UL 746B
Vicat Softening Temperature	240	°C	ISO 306/A
CLTE - Flow	2.5E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.40	W/m/K	DIN 52612

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer	100 - 140	°C
Hot air dryer, B	50 - 90	°C
Drying Time
Hot air dryer	2.0 - 4.0	hr
Hot air dryer, B	> 4.0	hr
Rear Temperature	300 - 320	°C
Middle Temperature	310 - 330	°C
Front Temperature	320 - 340	°C
Nozzle Temperature	320 - 340	°C
Processing (Melt) Temp	330	°C
Mold Temperature	150 - 180	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Category:	PPS , Polyphenylene Sulfide
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ubIZbV_LUVOCOM13018558.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SABIC® PP 527K	Saudi Basic Industries Corporation (SABIC)	PP Homopolymer	SABIC® PP
VENYL UG207 - 8071	AD majoris	Nylon 66	VENYL
Ebalta BLH Epoxy 200 / W 400	Ebalta Kunststoff GmbH	Epoxy	Ebalta
Ebalta MG 709-120 / Comp. A+B	Ebalta Kunststoff GmbH	PUR, Unspecified	Ebalta
HIPEX® HX8ICZ (Series: HTR/OR)	KRAIBURG TPE	TPE	HIPEX®