SLOVAMID® 6 BT
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uXTisu_SLOVAMID-6-BT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Basic type PA 6 for injection moulding, modified for general use, with excellent manufacturing properties. Use: automotive, engineering, electrical and consumer-goods industry - electrical tools, fasteners, clamps, hobby tools, toys. Delivered in the natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.8 | % | |
| Flow | 1.8 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.5 | kJ/m² | |
| 23°C | 1.6 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 80 | kJ/m² | |
| 23°C | 120 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 50.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 190 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® AZM-23-G9 | Arkema | Nylon 12 | Rilsan® |
| MAXAMID™ 403/450 NAT | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| POLYshine PBT D211 | Polykemi AB | PBT | POLYshine |
| Sylvin 8478-70FUV Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| MAJORIS MN300U BLACK 8229 | AD majoris | HDPE | MAJORIS |