Infino LT-1100
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uX3zsv_InfinoLT1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino LT-1100 is a polycarbonate (PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/10.0 kg | 25 | g/10 min | ASTM D1238, ISO 1133 |
| 300°C/1.2 kg | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.50 - 0.80 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.60 - 0.90 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.60 - 0.90 | % | ISO 2577 |
| Traffic : 3.20mm | 0.50 - 0.80 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 122 | ASTM D785 | |
| R scale | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 65.0 | MPa | ASTM D638 |
| Fracture | 64.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 110 | % | ASTM D638 |
| Fracture | 91 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 90.0 | MPa | ASTM D790 |
| -- 8 | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 78 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 850 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 23°C 10 | 69 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 137 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 135 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2700 S-30A Z | RTP Company | SEBS | RTP |
| Prime PETG 14471 | Primex Plastics Corporation | Unspecified | Prime PETG |
| Tecnoflon® FOR 537 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Toraycon® 1164G-15 T2 | Toray Resin Company | PBT | Toraycon® |
| Geon™ Vinyl Flexible XV3863 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |