ACCUTECH™ ABS832G10L
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uUTxeU_ACCUTECH-ABS832G10L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™ABS832G10L is an acrylonitrile butadiene styrene (ABS) product, and its filler is 10% glass fiber reinforced material. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.60 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 60.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3700 | MPa | ASTM D790 |
| Flexural Strength | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 96.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 86.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® F34 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Amilan® CM1014-V0 | Toray Resin Company | Nylon 66 | Amilan® |
| Formolon® 622F | Formosa Plastics Corporation, U.S.A. | PVC, Unspecified | Formolon® |
| Okirol® E-5 | DIOKI d.d. | PS (EPS) | Okirol® |
| Rotuba CAB B900 (22% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |