LNP™ THERMOCOMP™ QF007 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uU5wgr_LNPTHERMOCOMPQF007compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QF007 is a compound based on Nylon 6/10 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound QF-1007 Product reorder name: QF007 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 177 | MPa | ASTM D638 |
| Flexural Modulus | 8910 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PO Conc 62 | PolyOne Corporation | LDPE | Maxxam™ FR |
| Elvaloy® AC 1330 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |
| LONGLITE® PBT 3030-200S | CCP Group | PBT | LONGLITE® PBT |
| Petrothene® NA952083x01 | LyondellBasell Industries | LDPE | Petrothene® |
| TECACOMP® PA6 CF20 black 4097 | Ensinger GmbH | Nylon 6 | TECACOMP® |