Capilene® TG 50
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uTSvmm_Capilene-TG-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® TG 50 is a very high impact polypropylene heterophasic copolymer intended for injection molding. CAPILENE ® TG 50 features: excellent impact strength even at low temperature, optimized balance of stiffness and toughness. CAPILENE ® TG 50 is suitable for: technical items, closures, crates, boxes, luggage and toys. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 22.0 | MPa | ASTM D638 |
| Yield | 20.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 10 | % | ASTM D638 |
| Yield | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 975 | MPa | ASTM D790 |
| -- 3 | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C | 130 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -20°C | 8.0 | kJ/m² | ISO 180 |
| 23°C | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 70.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Forprene® 6NM001A90 | SO.F.TER. SPA | TPV | Forprene® |
| Karina COMP. PVC CRYSTAL -E 74/240-D-IS-SD-TR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8927 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Plaslube® PE 4000 LE | Techmer Engineered Solutions | UHMWPE | Plaslube® |
| ESTOPLAST XU 230BB04 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |