Spartech Polycom PP5440 is a polypropylene product, which contains a 40% glass fiber reinforced material. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 1.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ASTM D638 |
| Flexural Modulus - Secant | 5520 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Additional Information |
|---|
| Flexural Modulus, ASTM D790, Tangent: 1100000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 47-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Veroplas PA3150 | PlastxWorld Inc. | Nylon 6 | Veroplas |
| Bergamid™ A70 GK30 black 13539126 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Axiall PVC 10870 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hiprolon® 70 VN | Arkema | Nylon 610 | Hiprolon® |