Lupolen 4261 A Q 149
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Lupolen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uT6D63_Lupolen-4261-A-Q-149.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lupolen 4261 A Q149 is a high density polyethylene with an outstanding ESCR, good chemical resistance and high impact resistance. It is delivered in powder form without any additives. Typical customer applications include IBC, drums and jerry cans for the packaging of dangerous goods. Lupolen 4261 A Q149 is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| FNCT - 3.5 MPa, 2% Igepal BC/9 (80°C) | 2.5 | day | ISO 16770 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Staudinger Index | 370 | cm³/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 40.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 850 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (-30°C) | 170 | kJ/m² | ISO 8256/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 42.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 130 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 220 | °C |
| Extrusion instructions |
|---|
| Processing temperature range: 180 - 200 °C. As product does not contain antioxidants it should be processed at lowest possible temperature and by using inert gas in the hopper in order to reduce contact with oxygen which might lead to degradation. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8HAA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| XANTAR® 25 U | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Ultramid® 8231G HS | BASF Corporation | Nylon 6 | Ultramid® |
| VALOX™ K4530 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| POLYfill PPH GF4030 PD2 | Polykemi AB | PP Homopolymer | POLYfill |