DOW™ HDPE 05962B
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uNgrqo_DOW-HDPE-05962B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW HDPE 05962B is a High Density Polyethylene produced via SOLUTION™ technology. This resin presents a narrow molecular weight distribution that offers excellent impact resistance in rigid packaging, high gloss, excellent stiffness and processability. Main Characteristics
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (Compression Molded) | 44.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 29.0 | MPa | |
| Break, Compression Molded | 25.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 2400 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 110 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 24 | µm | |
| Film Puncture Resistance (24 µm) | 3.31 | J/cm³ | Internal Method |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 24 µm | 472 | MPa | |
| 2% Secant, TD : 24 µm | 672 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 24 µm | 27.0 | MPa | |
| TD : Yield, 24 µm | 28.0 | MPa | |
| MD : Break, 24 µm | 36.0 | MPa | |
| TD : Break, 24 µm | 28.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 24 µm | 600 | % | |
| TD : Break, 24 µm | 650 | % | |
| Dart Drop Impact (24 µm) | 8.0 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 24 µm | 40 | g | |
| TD : 24 µm | 120 | g |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 25 | J/m | ASTM D256 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 24.0 µm) | 85 | ASTM D2457 | |
| Haze (24.0 µm) | 6.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 268 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PR 79 T 30 | SILON s.ro | PP Copolymer | TABOREN |
| Borealis PE BB2581 | Borealis AG | HDPE | Borealis PE |
| DINALON® B1S25 G25XV0 | Grupo Repol | Nylon 6 | DINALON® |
| Ferro Nylon RNY20MA | Ferro Corporation | Nylon 66 | Ferro Nylon |
| Geon™ Vinyl Wire & Cable WY594B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |