KOPA® KN135G33BLHS1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uMwP9P_KOPA-KN135G33BLHS1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA® KN135G33BLHS1 is a Polyamide 6 (Nylon 6) product filled with glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 164 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9430 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 205 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® XL 400 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| Durethan® B 30 S FN40 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| KOPLA PA66 KDG1033RD | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Karina BLACK PVC COMPOUND TR-781-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9710-80FUV Blue 8335 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |