Novalloy-A A1500
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uLmG35_NovalloyAA1500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-A A1500 is an acrylonitrile butadiene styrene nylon (ABS nylon) material,. This product is available in the Asia-Pacific region,. The main characteristics of Novalloy-A A1500 are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.60 - 0.80 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | 101 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield) | 42.0 | 33.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1800 | 1200 | MPa | ISO 178 |
| Flexural Stress | 62.0 | 44.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 83 | 78 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | |||
| -30°C, 6.40 mm | 160 | -- | J/m | ASTM D256 |
| 23°C, 6.40 mm | 830 | 850 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 6.40mm | 100 | 92.0 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 100 | 90.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | 80.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.0 | 70.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Moisture Content | -- | 2.0 | % |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 220 - 250 | °C | |
| Front Temperature | 230 - 260 | °C | |
| Nozzle Temperature | 220 - 250 | °C | |
| Mold Temperature | 60.0 - 70.0 | °C | |
| Back Pressure | 10.0 - 20.0 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0437T30L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Ferro PP LPP20BN45HB BLACK | Ferro Corporation | PP Copolymer | Ferro PP |
| Generic PVDF | Generic | PVDF | Generic |
| Karina MBPEB ANTISPLIT - 1000/0080 IE | Karina Ind. e Com. de Plásticos Ltda | LDPE | Karina |
| Plenco 04300 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |