Riblene® FC 20
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uLXP75_Riblene-FC-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FC 20 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion. Riblene FC 20 is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 20 are easily heat shrinkable and characterised by optimum mechanical properties. Main Application Riblene FC 20 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 60 to 250 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 160 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 180 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 400 | % | |
| TD : Break, 70 µm, Blown Film | 550 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 290 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 25.0 | kN/m | |
| TD : 70.0 µm | 25.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 112 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 30 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 20 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207 D | RTP Company | Nylon 612 | RTP |
| VENYL UG308 | AD majoris | Nylon 66 | VENYL |
| WELLAMID Nylon 6600 GS 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Colorite CS Series CS9034SR | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Sylvin 3260-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |