Riteflex® 655HS
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Riteflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uIVc8G_Riteflex-655HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore D Hardness heat stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Specific Volume | 0.842 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.0 | % | ASTM D955 |
| Vertical flow direction | 1.7 - 2.1 | % | ISO 294-4 |
| Flow direction | 1.6 - 1.9 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 330 | % | ASTM D638 |
| Flexural Modulus (23°C) | 205 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 7.00 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Partial Break) | 65 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 178 | °C | ASTM D1525 |
| Peak Melting Temperature | 200 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 5.0E+12 | ohms·cm | ASTM D257 |
| -- | 2.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 1 | 14 | kV/mm | ASTM D149 |
| -- | 14 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.040 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 200 - 215 | °C | |
| Middle Temperature | 205 - 230 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Nozzle Temperature | 205 - 235 | °C | |
| Processing (Melt) Temp | 205 - 235 | °C | |
| Mold Temperature | 20.0 - 55.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 205 to 235°CZone 4 Temperature: 205 to 235°CFeed Temperature: 200 to 215°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PET EN230 | Guangdong Shunde Shunyan New Material Co., Ltd. | PET | Sunny® |
| THERMOLAST® K TC9FLN (Series: FR/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Badamid® LB75 K | Bada AG | Nylon 6 | Badamid® |
| Boda BDF-H2702 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Karina CLEAR PVC COMPOUND 105801/201-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |