Niplene F50 AGR
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niplene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uIPFod_Niplene-F50-AGR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, reinforced with 50% glass fibre chemically coupled to the polymeric matrix |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 0.30 to 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 110 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3 | 10500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 90 | J/m | |
| 23°C, 3.20 mm | 130 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 158 | °C | ASTM D648 |
| Vicat Softening Temperature | 146 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primolac V620GP | Lucent Polymers, Inc. | ABS | Primolac |
| YUPLENE® H930S | SK Global Chemical | PP Homopolymer | YUPLENE® |
| NYLEM® 6 GFR 30 | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| Formolene® L42009A | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Petrothene® YR19513 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |