Stat-Tech™ CTX-1125 Natural
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uH0oPC_Stat-Tech-CTX-1125-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.010 to 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation 1(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 109 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 10 to 1.0E+5 | ohms·cm | ASTM D257 |
| Charge Decay Time - (Mil-B-81705C), 12% RH, 5000kV to 50kV | 2 | msec | |
| Shielding Effectiveness | |||
| 10GHz, 1/8" thickness | 36 | dB | |
| 1GHz, 1/8" thickness | 16 | dB | |
| 5GHz, 1/8" thickness | 26 | dB |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (Internal Method) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3484 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Westlake LDPE EC477AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Karina IVORY PVC COMP. -E 750D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® NF1007F 10R | LG Chem Ltd. | PC | Lupoy® |
| SABIC® PPcompound 2609B | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |