TECHNYL® A 218 V20 BLACK 21 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uFLyYc_TECHNYL-A-218-V20-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA66, reinforced with 20% of glass fibre, heat stabilized, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7400 | 5300 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 145 | 100 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 4.0 | 5.0 | % | ISO 527-2/1A |
| Flexural Modulus | 6400 | 4200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 48 | 79 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 7.0 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 450 | 350 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTRATRAC® H950 | Haysite Reinforced Plastics | Polyester, TS | ULTRATRAC® |
| FHR EPS 55-7455 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Gallonprene® GP210-4504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KOPELEN J-370 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| PENTAMID A GV25 H UV natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |