Chemlon® 66GF6L Datasheet,Nylon 66,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
66GF6L is a 33% glass fibre reinforced nylon 66 that offers good mechanical performance, coupled with good surface finish and flow. It is a heat & light stabilised grade, suitable for extended use in outdoor, elevated service temperature applications.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	heat stabilizer UV stabilizer
Features	Light stabilization Good liquidity Good weather resistance Thermal Stability Excellent appearance
Uses	High temperature application Outdoor application
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.40	--	g/cm³	ISO 1183
Molding Shrinkage ¹	0.60 - 1.5	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.7	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	9500	7300	MPa	ISO 527-2
Tensile Stress	180	140	MPa	ISO 527-2
Tensile Strain (Break)	3.0	4.0	%	ISO 527-2
Flexural Modulus	9700	5800	MPa	ISO 178
Flexural Stress	270	150	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Unnotched Impact Strength	60 kJ/m²	No Break		ISO 179/1eU
Notched Izod Impact	12	35	kJ/m²	ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 240	--	°C	ISO 75-2/B
1.8 MPa, not annealed	240	--	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+14	1.0E+11	ohms	IEC 60093
Volume Resistivity	1.0E+16	1.0E+13	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	16	--	kV/mm	IEC 60243-1
Comparative Tracking Index	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	270 - 290	°C
Middle Temperature	270 - 290	°C
Front Temperature	270 - 290	°C
Processing (Melt) Temp	270 - 290	°C
Mold Temperature	80.0 - 90.0	°C
Injection Rate	Fast
Back Pressure	Low
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	uEtdKT_Chemlon-66GF6L.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SUPREME GPPS SC205	Supreme Petrochem Ltd.	PS (GPPS)	SUPREME GPPS
Bapolene® 4017	Bamberger Polymers, Inc.	PP Homopolymer	Bapolene®
Braskem PP HP 523J	Braskem	PP Homopolymer	Braskem PP
Epolene® N-30	Westlake Chemical Corporation	LDPE	Epolene®
Dryflex® VE 65A101	ELASTO	TPV	Dryflex®