AMPLIFY™ EA 101
| Category: | EEA , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ EA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uCPWl5_AMPLIFY-EA-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AMPLIFY™ EA 101 Functional Polymer is produced via a high-pressure reactor. This ethylene-ethyl acrylate (EEA) copolymer exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.931 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| Comonomer Content 1 | 18.5 | % | ASTM D3594 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 86 | ASTM D2240, ISO 868 | |
| Shaw D | 31 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 2.96 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 13.4 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 10 | % | ASTM D638, ISO 527-2 |
| Fracture | 750 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 55.2 | MPa | ASTM D790B, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 2 | 672 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 31.1 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 57.2 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 97.8 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 82.8 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行模塑和测试。 |
| Note Message | |
|---|---|
| 1 . | The calibration range is 15 - 20% EA; the path length has been standardized; the substrate/film thickness is 15 mil; the press temperature is 160°C |
| 2 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3582C | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC M1275 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Starex VH-0800 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Softell TKG 442N C12897 | LyondellBasell Industries | PP Copolymer | Softell |
| Sylvin 9604-90 Green 3201 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |