Witcom POM-C EC-EP-HI
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom POM-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uBXZ6V_Witcom-POM-C-EC-EP-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom POM-C EC-EP-HI is a polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 - 2.3 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 6.0 | % | ISO 527-2/50 |
| Flexural Modulus | 1800 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 6.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 75 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 105 | °C | ISO 75-2/A |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 170 - 210 | °C | |
| Mold Temperature | 50.0 - 120 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 HF | RTP Company | PEEK | RTP |
| TOTAL Polypropylene Aceso® PPM R020 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Nipol® NBR DN101 | Zeon Corporation | NBR | Nipol® NBR |
| Hyundai EP PA6 LS460 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| LNP™ THERMOCOMP™ RF005SXS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |