| WINTEC™ WFW4 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Film. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 7.0 | g/10 min | ISO 1133 |
| Spiral Flow | 46.0 | cm | Internal Method |
| Molding Shrinkage | 1.0 to 1.4 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | > 400 | % | ISO 527-2 |
| Flexural Modulus | 1000 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| 0°C | 1.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 90 | ASTM D523 | |
| Haze | ISO 14782 | ||
| 1000 µm | 25 | % | |
| 2000 µm | 60 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PP 1397 | Premix Oy | TPO | PRE-ELEC® |
| Sumiflex® K K58DL13 | Mitsubishi Chemical Corporation | PVC Elastomer | Sumiflex® K |
| TOTAL Polystyrene Crystal 1540 (AS) | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| Ultramid® A3HG6 HR | BASF Corporation | Nylon 66 | Ultramid® |
| Hostacom BB 1113 F BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |