Skyrol® SM30
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | uAqlIZ_Skyrol-SM30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SM30 is a transparent film with excellent handling characteristics. It is widely used in stamping foil, metallizing, metallic yarn, flexible packaging and adhesive tape applications. SM30 is highly resistant to "neckdown" or creasing caused by high-temperature, high-tension coating operations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | |||
| Flow : 190°C, 20 min, 0.0120 mm | 2.9 | % | Internal Method |
| Flow : 190°C, 20 min, 0.0230 mm | 2.3 | % | ASTM D955 |
| Flow : 190°C, 20 min, 0.0360 mm | 2.5 | % | ASTM D955 |
| Across Flow : 190°C, 20 min, 0.0120 mm | -0.10 | % | Internal Method |
| Across Flow : 190°C, 20 min, 0.0230 mm | 0.30 | % | ASTM D955 |
| Across Flow : 190°C, 20 min, 0.0360 mm | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.40 | ||
| vs. Itself - Dynamic 3 | 0.40 | ||
| vs. Itself - Dynamic 4 | 0.30 | ||
| vs. Itself - Static 5 | 0.50 | ||
| vs. Itself - Static 6 | 0.40 | ||
| vs. Itself - Static 7 | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 12 µm | 269 | MPa | |
| MD : Yield, 23 µm | 255 | MPa | |
| MD : Yield, 36 µm | 228 | MPa | |
| TD : Yield, 12 µm | 228 | MPa | |
| TD : Yield, 23 µm | 241 | MPa | |
| TD : Yield, 36 µm | 221 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 120 | % | |
| MD : Break, 23 µm | 130 | % | |
| MD : Break, 36 µm | 150 | % | |
| TD : Break, 12 µm | 130 | % | |
| TD : Break, 23 µm | 130 | % | |
| TD : Break, 36 µm | 140 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 12.0 µm | 164 | ||
| 23.0 µm | 163 | ||
| 36.0 µm | 161 | ||
| Transmittance | ASTM D1003 | ||
| 12.0 µm | 90.0 | % | |
| 23.0 µm | 90.0 | % | |
| 36.0 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 12.0 µm | 3.0 | % | |
| 23.0 µm | 3.6 | % | |
| 36.0 µm | 4.6 | % |
| Note Message | |
|---|---|
| 1 . | 36 µm |
| 2 . | 23 µm |
| 3 . | 12 µm |
| 4 . | 36 µm |
| 5 . | 12 µm |
| 6 . | 36 µm |
| 7 . | 23 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4909 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Starflam PK0032E | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| ACCUTECH™ CP0437T30L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Sylvin 9077-70 Grey 9556 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ SLX9271T resin | SABIC Innovative Plastics | PC | LEXAN™ |