Tenite™ Butyrate 572A1V95316 Smoke, Trsp
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tenite™ Butyrate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u8wT9W_Tenite-Butyrate-572A1V95316-Smoke-Trsp.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 572-16 contains an odor mask lubricant and an ultra-violet inhibitor (UVI). It has a plasticizer level of 16%. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 30.3 | MPa | |
| Break, 23°C | 31.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 26 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 100 | J/m | |
| 23°C | 530 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 79.0 | °C | |
| 1.8 MPa, Annealed | 67.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Loss on Heating - 72 hr (80°C) | 0.90 | % | ASTM D707 |
| Note Message | |
|---|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPUI-G95 | Taiwan PU Corporation | TPU-Capro | TPUCO® |
| Ferro PP WPP32SD03WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Elastron® V V601.A93.B | Elastron USA, Inc. | TPV | Elastron® V |
| LNP™ LUBRICOMP™ RI001 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Capilene® QC 56 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |