CYCOLOY™ XCM851 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u82fn7_CYCOLOY-XCM851-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4750 | MPa | ASTM D638 |
| -- | 4600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 35.0 | MPa | ASTM D638 |
| Fracture | 45.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5 |
| Fracture 5 | 12 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 4550 | MPa | ASTM D790 |
| -- 7 | 4400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| 23°C | 100 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13(23°C) | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 119 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 122 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ASTM D1525 15 |
| -- | 139 | °C | ISO 306/B50 |
| -- | 140 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 5.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 290 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Nozzle Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 195 - 205 | °C | |
| Cylinder Zone 2 Temp. | 200 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 240 | °C | |
| Cylinder Zone 4 Temp. | 230 - 260 | °C | |
| Adapter Temperature | 230 - 260 | °C | |
| Melt Temperature | 250 - 270 | °C | |
| Die Temperature | 230 - 245 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsRoll Stack Temp - Bottom: 145 - 155 °CRoll Stack Temp - Middle: 110 - 120 °CRoll Stack Temp - Top: 100 - 110 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 216 V40 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Unichem 81-001 | Colorite Polymers | PVC, Unspecified | Unichem |
| NEXT REGRIND PBT 420SEO-300RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| Nymax™ GF1200 A30 FR BK116 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Sylvin 5175-92 White 1472 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |