Clariant ABS ABS3400
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6uf30_Clariant-ABS-ABS3400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant ABS ABS3400 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America and is processed by injection molding. The main features of Clariant ABS ABS3400 are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 20 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 87.8 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256, Colors: 3.0 ft-lb/inNotched Izod Impact, ASTM D256, Black: 2.8 ft-lb/in |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 204 - 249 | °C | |
| Middle Temperature | 204 - 249 | °C | |
| Front Temperature | 204 - 249 | °C | |
| Processing (Melt) Temp | 204 - 246 | °C | |
| Melt Temperature (Aim) | 227 | °C | |
| Mold Temperature | 23.9 - 79.4 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 2.07 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| The minimum injection pressure to achieve 95% fill of the part during the boost injection pressure phase should be used. The hold pressure should be between 30% and 75% of the initial injection pressure. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 H TFE 20 SI 1 | RTP Company | Nylon 66 | RTP |
| TRAMID® 4110G33 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| VICTREX® HT™ 22CA30 | Victrex plc | PEK | VICTREX® HT™ |
| Hostacom TRC 152N KF | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ LUBRILOY™ DF204 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |