| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | PRIMALLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6uIyK_PRIMALLOY-B1942.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIMALLOY® B1942 is a Thermoplastic Elastomer (TPE) material. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 62 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 2.00 mm | 1.5 | % | |
| Flow : 2.00 mm | 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 48.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 670 | % | ISO 527-2 |
| Flexural Modulus | 420 | MPa | ISO 178 |
| Flexural Stress | 18.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 160 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 203 | °C | JIS K7206 2 |
| Note Message | |
|---|---|
| 1 . | 120x120x2 mm test plaque |
| 2 . | 50°C/h, A (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® GLT-600S | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| NEXUS Reprocessed PC 15/10 RBK | Nexus Resin Group, LLC. | PC | NEXUS Reprocessed |
| NEFTEKHIM PP 9240P | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Cellophane™ 500MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| OTECH PVC OE9529 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |