Lion Idemitsu Composites PPS G131L3
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u6Qai4_Lion-Idemitsu-Composites-PPS-G131L3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS G131L3 is a Polyphenylene Sulfide (PPS) product filled with 60% glass\mineral. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.20 | % | |
| Flow | 0.20 | % | |
| Water Absorption (23°C, 24 hr) | > 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 79.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.40 | % | ISO 527-2 |
| Flexural Modulus | 24300 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 6.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 281 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 9.0E-6 | cm/cm/°C | |
| Transverse | 1.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength (1.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 4.00 | IEC 60250 | |
| Dissipation Factor | 1.6E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 140 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-30G11-(V) | Polymer Technology and Services, LLC | PC+PBT | PTS |
| HIPREN® EM 1500 T | HIP-PetroHemija | SBR, Emulsion | HIPREN® |
| KumhoSunny PC/ABS HAC8265 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| LNP™ STAT-KON™ EX02598C compound | SABIC Innovative Plastics | PEI | LNP™ STAT-KON™ |
| API II 545 | API II, Inc. | PS (HIPS) | API II |