Celstran® PA6-GF40-01
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u5xmpK_Celstran-PA6-GF40-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% long strand glass fiber reinforced nylon 6 Natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 - 0.10 | % | ASTM D955 |
| Transverse flow | 0.25 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 11800 | MPa | ASTM D638 |
| 23°C | 13400 | MPa | ASTM D638 |
| 121°C | 7310 | MPa | ASTM D638 |
| -- | 12400 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 281 | MPa | ASTM D638 |
| Fracture, 23°C | 237 | MPa | ASTM D638 |
| Fracture, 121°C | 106 | MPa | ASTM D638 |
| Fracture | 205 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 2.6 | % | ASTM D638 |
| Fracture, 23°C | 2.5 | % | ASTM D638 |
| Fracture, 121°C | 3.0 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 11100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 335 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 32 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 265 - 275 | °C | |
| Middle Temperature | 270 - 275 | °C | |
| Front Temperature | 275 - 280 | °C | |
| Nozzle Temperature | 275 - 280 | °C | |
| Processing (Melt) Temp | 270 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 275 to 280°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Borealis PP HF420FB | Borealis AG | PP Homopolymer | Borealis PP |
| Geon™ Vinyl Flexible R8206A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Lucky Enpla LMA1000 | Lucky Enpla Co LTD | Acrylic (PMMA) | Lucky Enpla |
| Axiall PVC 8266 Natural 01 | Axiall Corporation | PVC, Rigid | Axiall PVC |