PALGLAS® R 07

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	pal plast GmbH
Trademark:	PALGLAS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	u4kDlr_PALGLAS-R-07.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
PALGLAS®R 07 is a polymethyl methacrylate-acrylic acid product,. It is available in Europe. Typical application areas are: electrical appliances. Features include: flame retardant/rated flame Heat resistance

General Information
Features	Good liquidity Heat resistance, medium
Uses	Electrical appliances
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	2.0	%	ISO 62
Equilibrium, 23°C, 50% RH	0.60	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	3000	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	70.0	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	3.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	18	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	102	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2900 to 3100 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 68 to 72 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 15 to 20 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 100 to 103 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.9 to 2.1 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.5 to 0.7 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2900 to 3100 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 68 to 72 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 2 to 5 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 15 to 20 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 100 to 103 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 1.9 to 2.1 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.5 to 0.7 %

Resin Grade	Manufacturer	Category	Trademark
Reon 67GER01	Reliance Industries Limited	PVC Homopolymer	Reon
APEX® 3310-60NT	Teknor Apex Company	PVC, Flexible	APEX®
Fainplast PVC GSK 74/UV	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
INSTRUC PPSBGF40IM	Infinity LTL Engineered Compounds	PPS	INSTRUC
Monprene® CP-15150D-10 NAT XRD1	Teknor Apex Company	TPE	Monprene®