AMPLIFY™ GR 205
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ GR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u4WAtY_AMPLIFY-GR-205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY™ GR 205 Functional Polymer is a maleic anhydride grafted (MAH) polymer. The base polymer is a high density polyethylene. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238, ISO 1133 |
| MAH Graft Level 1 | Very high | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 98 | ASTM D2240, ISO 868 | |
| Shaw D | 67 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture 2 | 15.9 | MPa | ASTM D638 |
| Fracture | 15.9 | MPa | ISO 527-2/51 |
| Tensile Elongation | |||
| Fracture 3 | 300 | % | ASTM D638 |
| Fracture | 300 | % | ISO 527-2/51 |
| Flexural Modulus - 2% Secant | 924 | MPa | ASTM D790A, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525, ISO 306 |
| Melting Temperature (DSC) | 130 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D4976 进行模塑。 |
| Note Message | |
|---|---|
| 1 . | Low:<0.25 wt %, medium 0.25-0.5 wt %, high> 0.5 wt %, very high> 1.0 wt% |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT HI2153 | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| LNP™ THERMOCOMP™ RF004XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Axiall PVC 4125-53 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Starex SV-0167 F | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |
| LNP™ THERMOCOMP™ DC0049XF compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |