Electrafil® PPS 06000
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u2r0Sg_Electrafil-PPS-06000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil® PPS 06000 is a Polyphenylene Sulfide (PPS) product filled with metallic flake. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 274 | °C | |
| 1.8 MPa, Unannealed | 260 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 | ohms | ASTM D257 |
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.399 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 316 to 343 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 316 to 332 | °C | |
| Processing (Melt) Temp | 324 to 338 | °C | |
| Mold Temperature | 129 to 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUGUARD™ CPO467V0CSV | ACLO Compounders Inc. | PP Copolymer | ACCUGUARD™ |
| ColorRx® PP2-0200RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| DAI-EL™ G-801 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina RED PVC COMPOUND 813D42/46-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LGG 1043 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGG |