VENELENE® 11U4
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u2SUtF_VENELENE-11U4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.4 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Film Puncture Force (35 µm) | 4.90 | N | ASTM D3420 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 35 µm | 34.0 | MPa | ASTM D882 |
| TD : Fracture, 35 µm | 26.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 35 µm | 700 | % | ASTM D882 |
| TD : Fracture, 35 µm | 800 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 35 µm | 250 | g | ASTM D1922 |
| TD : 35 µm | 350 | g | ASTM D1922 |
| Impact Resistance, Film | 190 | J/cm | ASTM D1709 |
| Toughness, Film | ASTM D882 | ||
| MD | 130 | MPa | ASTM D882 |
| TD | 145 | MPa | ASTM D882 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (35.0 µm) | 71.0 | % | ASTM D1003 |
| Haze (35.0 µm) | 24 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Extrusion instructions |
|---|
| Inverted Extrusion profile (descendent). Blow up ratio (BUR): 2 - 3 Die gap: 0.9 -1.2mm Frost line Height (ALE): 4 - 5 times die diameter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 5 Series 582A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| Titacon® TX915 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| LNP™ THERMOCOMP™ DX06409 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| NYLOY® KF-0030N 313WT | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| ULTEM™ 1100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |