Ateva® 1820
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u2BiHR_Ateva-1820.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive, foam, and compounding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 15.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 680 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 52.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 87.0 | °C | ASTM D3418 |
| Ring and Ball Softening Point | 172 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 1001C White Opaque | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Vydyne® R515 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Fainplast PVC PK 5510 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| RTP 1899 X 136863 K | RTP Company | Acrylic (PMMA) | RTP |
| Sylvin 8699-75 Clear Blue 8434 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |