NYCOA Polyamide ASN 27 330 KNF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u23CoV_NYCOA-Polyamide-ASN-27-330-KNF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA ASN 27/330 KNF is a 33% glass fiber reinforced, heat stabilized Nylon 6 resin used for injection molding. This grade offers an excellent balance of mechanical properties. NYCOA ASN 27/330 KNF is available in UV stable, custom colors, and impact modified grades. It also has excellent chemical resistance to greases, oils, and other hydrocarbons. Typical applications include automotive pedals, weed trimmer heads, and speaker brackets. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 9560 | MPa | ASTM D638 |
| Tensile Strength 2 | 175 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 8730 | MPa | ASTM D790 |
| Flexural Strength 5 | 260 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 220 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Melting Temperature | 222 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 232 - 271 | °C | |
| Middle Temperature | 243 - 282 | °C | |
| Front Temperature | 254 - 291 | °C | |
| Nozzle Temperature | 252 - 291 | °C | |
| Processing (Melt) Temp | 254 - 291 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1312 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Sinpolene MBW105LE | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Vital-Line SHE11155G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Latamid 12 H2 G/30 | LATI S.p.A. | Nylon 12 | Latamid |
| LNP™ STAT-KON™ DE002 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |