Latan 13 S/30
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u0nPV9_Latan-13-S-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyoximethylene (POM). Glass beads. Product UL certified. Medium viscosity. Good dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.7 to 2.0 | % | |
| Flow : 2.00 mm | 1.7 to 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 3600 | MPa | |
| 60°C | 2300 | MPa | |
| 90°C | 1300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 35.0 | MPa | |
| Yield, 60°C | 25.0 | MPa | |
| Yield, 90°C | 20.0 | MPa | |
| Break, 23°C | 35.0 | MPa | |
| Break, 60°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Yield, 60°C | 6.0 | % | |
| Yield, 90°C | 7.0 | % | |
| Break, 23°C | 20 | % | |
| Break, 60°C | 65 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 1.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 40 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 30 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 80.0 | °C | |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1626 (Punching) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Witcom ABS 3S | Witcom Engineering Plastics B.V. | ABS | Witcom ABS |
| ACCUTECH™ CP0436C40L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| DynaChar™ 5565-C | Polymer Dynamix | TPE | DynaChar™ |
| ENFLEX S3350A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |