Devcon Titanium Putty
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | u0OAuO_Devcon-Titanium-Putty.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High-tech, titanium-reinforced epoxy putty engineered for making critical repairs to machinery and precision parts. Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement | |
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.36 | g/cm³ | |
| Specific Volume | 0.423 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 177 | °C | |
| Wet | 66 | °C | |
| Tensile Shear Adhesion | 13.8 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6550 | MPa | ASTM D638 |
| Flexural Strength | 53.1 | MPa | ASTM D790 |
| Compressive Strength | 105 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.82 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 2.2 | kV/mm | ASTM D149 |
| Dielectric Constant | 44.8 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 4.3 Mixing ratio by capacity: 3.1 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 21 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 7010F-600 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Envirez® SS 70419 | Ashland Performance Materials | Polyester, TS | Envirez® |
| Keliren® XH-SJ | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| LUVOCOM® 80/TF/18/NT | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| POLYabs N20 | Polykemi AB | ABS | POLYabs |