TRANSMARE® 19HGF50-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | twuBmG_TRANSMARE-19HGF50-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HGF50-0.001 is a 50% glass fiber reinforced polypropylene homopolymer for injection molding purposes with very high stiffness and a good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 2.5 | g/10 min | |
| 230°C/5.0 kg | 13 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 4.00 mm) | 125 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 2.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 12000 | MPa | ISO 178 |
| Flexural Stress 2 | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 8.5 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 11 | kJ/m² | |
| 23°C | 13 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 146 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 161 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Battery GPP1001V0M-HCO-15 | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| Toughblend® PBT-1200 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Toughblend® |
| LNP™ STAT-KON™ RE003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| MAJ'ECO EEP364M - 8229 | AD majoris | PP, Unspecified | MAJ'ECO |
| TECHNYL® A 20 V25 BLACK 2006 CF | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |