LNP™ LUBRICOMP™ LFL36E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | twFxth_LNP-LUBRICOMP-LFL36E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP LFL36E is a compound based on Polyetheretherketone containing 30% Glass Fiber, 15% PTFE. Added features of this material are: Wear Resistant, Easy Molding. Also known as: LNP* LUBRICOMP* Compound LFL-4036 EM Product reorder name: LFL36E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 176 | MPa | ASTM D638 |
| Break 2 | 170 | MPa | ASTM D638 |
| Break | 177 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 2.0 | % | ASTM D638 |
| Break 4 | 2.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 11700 | MPa | ASTM D790 |
| -- 6 | 11400 | MPa | ISO 178 |
| Flexural Strength 7(Break, 50.0 mm Span) | 263 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.49 | ||
| vs. Itself - Static | 0.73 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 9.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 64.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 860 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 13.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 339 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 337 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 327 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 322 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VA10300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| Chemlon® 113 GHIU BK156 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hanwha Total PE 431G | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| HiFill® PA6 0325 | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LUVOCOM® 80-7858-B | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |