Order Products : sales@su-jiao.com
RTP 283A HEC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvrzxq_RTP-283A-HEC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm, Injection Molded) | 0.20 - 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 10300 | MPa | ASTM D638 |
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 1.5 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 8270 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 193 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 0.10 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Static Decay MIL-PRF-81705D, FTMS-4046.1: <2 sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 221 - 271 | °C | |
| Middle Temperature | 221 - 271 | °C | |
| Front Temperature | 221 - 271 | °C | |
| Mold Temperature | 54.0 - 93.0 | °C | |
| Injection Pressure | 69.0 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMPLIFY™ TY 1054H | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| Daelim Po1y® LH-4100SK | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DOMAMID® A1-009-V25-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Iupilon® EFT2200 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LEXAN™ ML3260 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |