Daelim Po1y® LL-05S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvqQDk_Daelim-Po1y-LL-05S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®LL-05S is a linear low density polyethylene product, and the filler is glass fiber reinforced material. It is available in the Asia-Pacific region. Daelim Po1y®LL-05S application areas include film and food contact applications. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 12.7 | MPa | ASTM D882 |
| TD : Yield | 10.8 | MPa | ASTM D882 |
| MD : Fracture | 36.3 | MPa | ASTM D882 |
| TD : Fracture | 30.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 600 | % | ASTM D882 |
| TD : Fracture | 800 | % | ASTM D882 |
| Dart Drop Impact | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 2.0 | g | ASTM D1922 |
| TD | 9.0 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Tear Strength, MD, ASTM D-1004: 105kg/cmTear Strength, TD, ASTM D-1004: 95kg/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 170 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA6 HI BLK | RTP Company | Nylon 6 | RTP |
| TECHNAMID® A A-SV30-npR | Poly Plastic | Nylon 66 | TECHNAMID® A |
| TOTAL Polyethylene HDPE 2008 SN 60 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Karina BLACK PVC COMPOUND 802D48/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ ZFM62P compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |