PENTAMID AB S GV60 H natural
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvIsND_PENTAMIDABSGV60Hnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, heat stabilised polyamide 66+6,60% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.35 | % | ISO 294-4 |
| Flow | 0.20 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ISO 62 |
| Viscosity Number | 140 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 235 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | 15000 | MPa | ISO 178 |
| Flexural Stress | 350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ISO 75-2/A |
| Melting Temperature | 255 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.6 mm | HB | UL 94 | |
| 3.2 mm | HB | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA66+PA6, MHR, 12-180 N, GF60 | ISO 1874 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 275 - 295 | °C | |
| Middle Temperature | 280 - 305 | °C | |
| Front Temperature | 285 - 295 | °C | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 80.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFC7000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Stirolan DF AE V0 1.6 | Soredi S.p.a. | PS (HIPS) | Stirolan |
| Network Polymers PS HIPS 90 0802 | Network Polymers, Inc. | PS (HIPS) | Network Polymers PS |
| DINALON® PA 6.6 IGNÍFUGA 30% FV | Grupo Repol | Nylon 66 | DINALON® |
| EZPrene 9565A SHF | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |