Stratasys Digital ABS
| Category: | Unspecified , Unspecified |
| Manufacturer: | Stratasys |
| Trademark: | Stratasys |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tvGfGE_Stratasys-Digital-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Our Digital ABS family offers toughness combined with exceptional dimensional stability. This material is offered in green and ivory and is fabricated from two base materials: RGD515 and RGD535 Green or RGD531 Ivory. It is designed to simulate ABS engineering plastics by combining strength with high-temperature resistance. Digital ABS is suitable for simulating parts that require high impact resistance and shock absorption with it's impact resistance of 65-80J/m (1.22-1.5 ft lb/inch) and a heat deflection temperature of (HDT) of 58-68 °C (136-154 °F). A higher HDT of 82-95 °C (179-203 °F) can be achieved after thermal post- treatment in a programmable oven using different temperature profiles. Ideal for:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 to 1.18 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 67 to 69 | ||
| Durometer Hardness (Shore D) | 85 to 87 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 to 3000 | MPa | ASTM D638 |
| Tensile Strength | 55.0 to 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 to 40 | % | ASTM D638 |
| Flexural Modulus | 1700 to 2200 | MPa | ASTM D790 |
| Flexural Strength | 65.0 to 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 65 to 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed 1 | 82.0 to 90.0 | °C | |
| 0.45 MPa, Unannealed 2 | 92.0 to 95.0 | °C | |
| 0.45 MPa, Unannealed | 58.0 to 68.0 | °C | |
| 1.8 MPa, Unannealed | 51.0 to 55.0 | °C | |
| Glass Transition Temperature | 47.0 to 53.0 | °C | DMA |
| Note Message | |
|---|---|
| 1 . | After thermal post treatment procedure A |
| 2 . | After thermal post treatment procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVODE 190 | Zhejiang Hisun Biomaterials Co.,Ltd | PLA | REVODE |
| Witcom PA66 3A/2L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Ultramid® B33 01 | BASF Corporation | Nylon 6 | Ultramid® |
| Axpoly® r-PS01 1064 | Axion Polymers | PS (HIPS) | Axpoly® |
| DOMAMID® 66G30HR | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |