VALOX™ 215HPR resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tt09bw_VALOX-215HPR-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced PBT with mold release. FDA food contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility data. Alternative grade VALOX HX215HP. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Specific Volume | 0.770 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.90 to 1.6 | % | |
| Flow 2 | 1.5 to 2.3 | % | |
| Across Flow 3 | 1.0 to 1.7 | % | |
| Across Flow 4 | 1.6 to 2.4 | % | |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5(Yield) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 6(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 7(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Gardner Impact 9(23°C) | 40.7 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 154 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 54.4 | °C | |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 8.1E-5 | cm/cm/°C | |
| 60 to 138°C | 1.4E-4 | cm/cm/°C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 110 | Pa·s | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Nozzle Temperature | 238 to 254 | °C | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | Modified |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 47-88 G2 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| THERMOLAST® K TF8WKF (Series: DW) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Vi-Chem PVC V143-90I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Adell Polyamide AD-10 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Axiall PVC 7456 | Axiall Corporation | PVC, Rigid | Axiall PVC |