TROGAMID® T T5002

Category:	Nylon 6/3T , Polyamide 6/3T Copolymer
Manufacturer:	Evonik Industries AG
Trademark:	TROGAMID® T
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tqeSlZ_TROGAMID-T-T5002.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp.

In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles.

TROGAMID® T5002
Permanently transparent polyamide with internal mold release agent for injection molding, extrusion, and blow molding.

General Information
Additive	Mold Release
Features	Amorphous Copolymer Good Chemical Resistance Good Electrical Properties Good Mold Release Good Thermal Stability High Viscosity Low Shrinkage Low Warpage
Uses	Electrical/Electronic Applications Filters Gears Machine/Mechanical Parts
Appearance	Clear/Transparent Colors Available Natural Color
Processing Method	Blow Molding Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.12	g/cm³	ISO 1183
Viscosity Number	125	cm³/g	ISO 307

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	86		ISO 868
Ball Indentation Hardness	155	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2800	MPa	ISO 527-2
Tensile Stress (Yield)	90.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	8.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	> 50	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	2500	MPa
1000 hr	1300	MPa
Flexural Modulus	3000	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C, Complete Break	6.0	kJ/m²
0°C, Complete Break	9.0	kJ/m²
23°C, Complete Break	10	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
0°C	No Break
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	145	°C	ISO 75-2/B
1.8 MPa, Unannealed	130	°C	ISO 75-2/A
Glass Transition Temperature ¹	150	°C	ISO 11357-2
Vicat Softening Temperature
--	155	°C	ISO 306/A
--	150	°C	ISO 306/B
CLTE			ISO 11359-2
Flow : 23 to 80°C	5.5E-5	cm/cm/°C
Transverse : 23 to 80°C	5.5E-5	cm/cm/°C
RTI Elec			UL 746
1.60 mm	100	°C
3.00 mm	100	°C
RTI Imp			UL 746
1.60 mm	80.0	°C
3.00 mm	85.0	°C
RTI Str			UL 746
1.60 mm	85.0	°C
3.00 mm	90.0	°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Electric Strength	26	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 50 Hz	4.00
23°C, 1 MHz	3.70
23°C, 100 MHz	4.30
Dissipation Factor			IEC 60250
23°C, 50 Hz	0.018
23°C, 1 MHz	0.026
Comparative Tracking Index			IEC 60112
-- ²	575	V
Solution A	600	V

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	V-2
1.60 mm	V-2
Glow Wire Flammability Index (1.00 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.00 mm)	850	°C	IEC 60695-2-13

Note Message
1 .	10 K/min
2 .	100 drops value

Resin Grade	Manufacturer	Category	Trademark
Matrixx 14A4152	The Matrixx Group, Inc.	PP, Unspecified	Matrixx
RTP 1403 N L	RTP Company	PESU	RTP
Tru-Bond™ PSA 3000	Devcon	Acrylic, Unspecified	Tru-Bond™
HOPELEN J-160	Lotte Chemical Corporation	PP Homopolymer	HOPELEN
EPAMOULD 295A10T	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD