TOTAL Polyethylene EVA 1020 VN 5
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tqLYP0_TOTAL-Polyethylene-EVA-1020-VN-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVA 1020 VN 5 is made by a high pressure tubular process. Grade for very flexible films with very high transparency and good mechanical properties. Application examples: chemicals bags, coextrusion films. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 0.940 | g/cm³ | ISO 1183 |
| -- | 940 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Melt volume-flow rate (190°C/2.16 kg) | 2.50 | cm³/10min | ISO 1133 2 |
| Vinyl Acetate Content | 17.5 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 25 | % | ISO 527-2 3 |
| Tensile Elongation at Break | > 50 | % | ISO 527-2 4 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 5.60 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 4.60 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 29.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 28.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 330 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 620 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 500 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 64.0 | °C | ISO 306 |
| 50°C/h, B (50N) | 62.0 | °C | ISO 306 5 |
| Melting Temperature (DSC) | 87.0 | °C | ISO 3146 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Elmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 26 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 43 N/mmHaze, ISO 14782, Blown Film, 40 µm: 1.5% |
| Extrusion instructions |
|---|
| Advised Temperature Profile: 150 to 180°CPossible Range of Thicknesses: 20 to 100 µ |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3740 | Prime Polymer Co., Ltd. | PP Random Copolymer | PRIME TPO |
| AIE ABS 2010AF | Asia International Enterprise (Hong Kong) Limited | ABS | AIE ABS |
| Aurora PVC AP3310 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Kingfa HR-527 | Kingfa | ABS | Kingfa |
| INSPIRE™ TF2301 ESU | Trinseo | PP, Unspecified | INSPIRE™ |