RIALOX® B 120 GF30 ST F V-0 natural
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | RIA-Polymers GmbH |
| Trademark: | RIALOX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | toc9DD_RIALOX-B-120-GF30-ST-F-V-0-natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIALOX B 120 GF30 ST F V-0 natural is a semi-crystalline thermoplastic flame-retardant construction material based on polybutylene terephthalate (PBT), reinforced with 30% glass fibers. RIALOX B 120 GF30 ST F V-0 natural will be processed by injection molding. It is used for parts for which a halogen-free PBT with fire protection equipment is required. The product is available in all colours. RIALOX B 120 GF30 ST F V-0 natural is characterized by the following properties:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 3.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Flow direction | 0.10 - 0.40 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 224 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 212 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 193 | °C | ISO 306/B50 |
| Maximum Operating Temperature | |||
| Continuous | 150 | °C | |
| Short Time | 200 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.90 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.00 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 775 | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Mechanical values determined after storage > 16 h at standard conditioning atmosphere (23 °C / 50 % rel. h.) |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Hopper Temperature | 50.0 - 70.0 | °C | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 250 - 270 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 5.00 - 10.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID B 280 R2 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Flextuff® S2801-00-E | Noble Polymers | TPE | Flextuff® |
| Hydrin® T3108 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| LONGLITE® PET 9030-200 | CCP Group | PET | LONGLITE® PET |
| Stat-Tech™ PA66 C20 black (EM00000364BI) | PolyOne Corporation | Nylon 66 | Stat-Tech™ |