Megatron® PPS-GF40R
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Mega Polymers |
| Trademark: | Megatron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | toGQGZ_Megatron-PPS-GF40R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyphenylene Sulfide 40% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 to 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 1450 | MPa | ASTM D790 |
| Flexural Strength | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 280 | °C | |
| 1.8 MPa, Unannealed | 267 | °C | |
| Continuous Use Temperature | 220 | °C | UL 746 |
| Melting Temperature | 280 | °C | ISO 11357-3 |
| RTI Imp | 220 | °C | UL 746 |
| RTI Str | 225 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 140 HI Z | RTP Company | PP, Unspecified | RTP |
| Mecoline I RDX 5210 F | Melos GmbH | TP, Unspecified | Mecoline |
| VITAMIDE® AT36GY6473 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Kazan LDPE 16214-020 OKP 22 111 3403 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| Karina HONEY PVC COMP -E TR 500D22/173 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |