Toyolac® 100G-23R
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tmI9Np_Toyolac-100G-23R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 100G-23R is an Acrylonitrile Butadiene Styrene (ABS) product filled with 23% glass bead\glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 | g/cm³ | ASTM D792 |
| 23°C | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 37 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 88.0 | MPa | ASTM D638 |
| 23°C | 84.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6700 | MPa | ASTM D790 |
| 23°C | 6290 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 127 | MPa | ASTM D790 |
| 23°C | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 77 | J/m | |
| 23°C, 12.7 mm | 63 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom X02475 | Spartech Polycom | PP Homopolymer | Spartech |
| Nylfor® A2 FR1/2A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Evoprene™ 689 | AlphaGary | SBS | Evoprene™ |
| Hyundai EP PPF HT340 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Sylvin 8200-90 White 1569 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |