Marlex® D173
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | thPg1l_MarlexD173.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This metallocene linear low density polyethylene is an ethylene-hexene copolymer tailored for cast film applications that require:
Typical cast film applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Cast Film) | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, cast film | 103 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, cast film | 110 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, extruded film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, extruded film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 25 µm, extruded film | 54.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 38.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 580 | % | ASTM D882 |
| Seal Initiation Temperature (25 µm, Cast Film) | 101 | °C | ASTM F88 |
| Dart Drop Test (25.4 µm) 1 | 173.7 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 25.4 µm | 115.8 | kN/m | ASTM D1922 |
| TD : 25.4 µm | 193.0 | kN/m | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm, Blown Film) | 140 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SURPASS® IGs153-A | NOVA Chemicals | HDPE Copolymer | SURPASS® |
| Akulon® N24-G8 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Fainplast PVC RKS 310/K1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Lotader® 8200 | Arkema | EEA | Lotader® |
| Sylvin 86052-80 Clear 8492 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |