TAROMID A 280 G5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgppy8_TAROMID-A-280-G5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 medium viscosity glass fiber reinforced 25%, good mechanical and thermal properties. UL94 HB approuved at 0,75 mm - NC Available: all colors, UV-stabilized (L), heat stabilized (H), release agent (W),laser printable (LP). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 to 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.50 | % | |
| Across Flow | 1.0 to 1.4 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.80 | % | ASTM D570, ISO 62 |
| Saturation | 5.5 | % | ASTM D570 |
| Saturation, 23°C | 5.5 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 146 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 230 | MPa | ISO 178 |
| Break | 230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 6.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 36 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 3 | 100 | °C | |
| -- 4 | 130 | °C | |
| -- 5 | 140 | °C | |
| -- 6 | 180 | °C | |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50, ASTM D1525 7 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Heat Stabilized, 20000 hrs |
| 5 . | Short Term |
| 6 . | Heat Stabilized, Short Term |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3590 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Armlen® PP HC 30 | Poly Plastic | PP, Unspecified | Armlen® |
| Ebalta AH 110 / TGS | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Mafill® HF 4002 | Ravago Group | PP Homopolymer | Mafill® |
| Durez® 33118 | SBHPP | Phenolic | Durez® |