TECACOMP® PPS CF40 black 9736
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgcLCy_TECACOMPPPSCF40black9736.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECACOMP®PPS CF40 black 9736 is a polyphenylene sulfide (PPS) product, which contains 40% carbon fiber reinforcement. It can be processed by injection molding and is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | |
| Apparent Density | 0.56 | g/cm³ | ISO 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 29000 | MPa | ISO 527-2/50 |
| Tensile Stress | 200 | MPa | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 28 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 90.0 | °C | DIN 53765 |
| Melting Temperature | 280 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 150 to 250°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 150 to 250°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Service Temperature | |||
| long term | 230 | °C | |
| short term | 260 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electrical Conductivity | 65.0 | S/m | ISO 3915 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.5 | ohms·cm | ISO 3915 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 300 - 370 | °C | |
| Mold Temperature | 140 - 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAKEEP® Film 0FH80 | Evonik Industries AG | PEEK | VESTAKEEP® Film |
| TPUCO® TPUE-UE90 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Lotryl® 24MA02 | Arkema | EMA | Lotryl® |
| O'Tech OW 641 ABFR | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Pearlbond™ 580 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlbond™ |